Series 22 | Epoxoline

Generic Type Modified Polyamine Epoxy
Common Usage An advanced generation, 100% solids, high-build epoxy for the protection of steel and concrete. It provides excellent resistance to abrasion and is suitable for immersion service. Specialized curing mechanism allows for faster cure response with airless spray application.
Colors WH11 Off-White, 1218 Light Blue, 1255 Beige
Finish Semi-Gloss
Surfacer/Filler/Patcher Series 215, 217, 218
Primers Steel: Self-priming, 66, L69, L69F, N69, N69F, V69, V69F, 90-97, H90-97, 90G-1K97, H91-H2O, 94-H2O, L140, L140F, N140, N140F, V140, V140F, 161
Topcoats Series 73, 740, 750, 1028, 1029, 1074, 1074U, 1075, 1075U, 1080, 1081. Note: Series 22 exterior (sunlight) exposed for longer than maximum recoat requires scarification by abrasive blasting prior to topcoating.
Volume Solids 100% (mixed) †
Recommended DFT 16 to 30 mils (405 to 762 microns) in one or two coats.
Curing Time
Temperature To Touch Dry Through Minimum to Recoat Return to Service Maximum to Recoat
95°F (35°C)2 1/2 hours5 1/2 hours4 hours5 days7 days
75°F (24°C)7 hours18 hours16 hours5 days7 days
50°F (10°C)24 hours27 hours32 hours7 days7 days
Note: These times are based on 20.0 mil (500 micron) dry film thickness. Cure time varies with surface temperature, air movement, humidity, and film thickness. Ventilation: When used as a tank lining or in enclosed areas, provide adequate ventilation during application and cure.
Volatile Organic Compounds Unthinned: 0.10 lbs/gallon (12 grams/litre)
Thinned 5%: 0.44 lbs/gallon (52 grams/litre) †
HAPS Unthinned: 0.0 lbs/gal solids
Thinned 5%: 0.37 lbs/gal solids
Theoretical Coverage 1,604 mil sq ft/gal (39.4 m²/L at 25 microns). See APPLICATION for coverage rates. †
Number of Components Two: Part A (polyamine) and Part B (epoxy)